POLYPROPYLENE COPOLYMER
EXTRUSION GRADE

PPCP EP-D 60 R

PARAMETER TEST METHOD VALUE UNIT
Melt flow rate (230 °C, 2.16 kg) ISO 1133 0.4 dg / min
Density ISO 1183 0.9 g/cm3  
Flexural modulus ISO 178 1050 N/mm2
Tensile strength yield ISO R 527 26 N/mm2
Elongation at yield ISO R 527 16 %
Izod Impact Strength (notched) at 23°C ISO 180 60 kJ/m2
Hardness Shore D ISO 868 60 Points
Vicat softening point (9.8 N) ISO 306/A 151 °C
H.D.T. (0.46 Mpa) ISO 75/B 88 °C
Accelerated oven ageing in air

(forced circulation) at 150 °C

ISO 4577 1800 hours
APPLICATIONS

Extrusion blow molding appliance components, wheels, under-the-hood automotive parts, toolboxes, suitcases and large containers, profiles, pipes and tough sheet for industrial applications