HIGH DENSITY POLYETHYLENE
FILM EXTRUSION

HDPE 7000F (ILCO)

PARAMETER TEST METHOD UNIT VALUE
Melt flow rate ISO 1133 g/10 min. 0.04
Density ISO 1183 kg/m3 952
Tensile Strength at yield ISO 527-1, -2 MPa 27
Tensile Strength at break ISO 527-1, -2 MPa >24
Elongation at Break ISO 527-1, -2 % >500
Charpy Impact strength ISO 179-1 kJ/m2 NB
Shore hardness ISO 868 D scale 64
Stress cracking resistance ASTM 1693 hr >600
Melting temperature ISO 11357 ºC 131
Vicat softening temperature ISO 306 ºC 124

HIGH DENSITY POLYETHYLENE
FILM EXTRUSION

HDPE 7000F (MRCO)

PARAMETER TEST METHOD VALUE UNIT
Melt flow rate ASTM D 1238 @ 190 °C, 2.16 kg 0.04 g/10 min
Density ASTM D 1505 0.954 g/cm3
Melting Point ASTM D 2117 131 °C
Vicat Softening Point ASTM D 1525 124 °C
Brittleness Temperature ASTM D 746 < -60 °C
ESCR ASTM D 1693 @ 50 °C > 1000 hrs,F50
Tensile Strength at yield ASTM D 638 @crosshead speed 50 mm /min MD:_*,TD:250* kg/cm2
Tensile Strength at break ASTM D 638 @crosshead speed 50 mm /min MD:620*,TD:310* kg/cm2
Tensile Modulus, 2% secant ASTM D 638 @crosshead speed 50 mm /min MD:8200*,TD:8000* kg/cm2
Elongation at Break ASTM D 638 @crosshead speed 50 mm /min MD:240*,TD:450* %
Elmendorf Tear Strength ASTM D 1922 MD:3*,TD:80* g
Dart Impact Strength ASTM D 1709 139* g
APPLICATIONS

Excellent mechanical strength and high stiffness Excellent processability (at high speed) Tissue-like film, garment/grocery/merchandise bags, disposal waste bags, counter bags, grocery sacks, trash bags